NYLENE 204 HS
TECHNICAL DATA SHEET

 
General Description    

  • Heat stabilized version general purpose, fast cycling molding resin
  • Crystallization initiators provide fast molding cycles through rapid melt set-up
  • In addition to protection from heat degradation, parts molded from NYLENE 204 HS have better dimensional stability at moisture equilibrium than parts molded from conventional nylon
  • Suitable for molding clip and fasteners, bushings, spacers, and other general purpose applications
 

Properties   

Physical Properties
Test Method
Units
Dry as Molded
Specific Gravity
D792
1.13
Mold Shrinkage
in/in
0.009
 
Mechanical Properties
Test Method
Units
Dry as Molded
Tensile Strength
D638
psi MPa
11,500 (79)
Elongation
D 638
%
60
Flexural Modulus
D 790
psi MPa
400,000 (2760)
Notched Izod @ 23 °C
D256
ft. lb./ in. J/m
0.9 (48)
 
Thermal Properties Test Method Units
Dry as Molded
DTUL @ 1820 KPa
D 648
°F °C
150 (66)
DTUL @ 455 KPa
D 648
°F °C
347 (175)
Melt Point
D3418
°F °C
420 215
 
Testing conducted on dry-as-molded specimens at 73°F
 
Notes
All values are for dry as molded specimens. The data set forth herein has been carefully compiled by Polymeric Resources Corporation. Values shown are typical properties and are not for specification. Since processing variables will affect properties, the reproducibility of our data in a customer's facility is not guaranteed. There is no warranty of any kind either expressed or implied, applicable to the use of this information, and the user assumes all risk and liability in connection therewith.



Issued: 2009/09/23