NYLENE PX3422
TECHNICAL DATA SHEET

 
General Description    

  • Heat stabilized, high impact modified nylon resin designed for maximum toughness with minimum sacrifice in tensile strength and melting point
  • Offers outstanding elongation and good retention of that elongation after 5 days of heat aging at 177°C (95% elongation)
  • Optimum processing conditions should provide a melt temperature of 490 - 530°F at the die
  • Suitable for processing in either extrusion or injection molding applications
 

Properties   

Physical Properties
Test Method
Units
Dry as Molded
Specific Gravity
D792
1.07
 
Mechanical Properties
Test Method
Units
Dry as Molded
Tensile Strength
D638
psi MPa
6,400 (45)
Elongation at Break
D638
%
310
Flexural Modulus
D790
psi MPa
210,000 (1,450)
Notched Izod @ 23 °C
D256
ft. lb./ in. J/m
20.0 (1,070)
 
Thermal Properties Test Method Units
Dry as Molded
DTUL @ 1820 kPa
D648
°F °C
108 (42)
Melt Point
D3418
°F °C
417 (214)
 
Testing conducted on dry-as-molded specimens at 73°F
 
Notes
All values are for dry as molded specimens. The data set forth herein has been carefully compiled by Polymeric Resources Corporation. Values shown are typical properties and are not for specification. Since processing variables will affect properties, the reproducibility of our data in a customer's facility is not guaranteed. There is no warranty of any kind either expressed or implied, applicable to the use of this information, and the user assumes all risk and liability in connection therewith.



Issued: 2009/09/23