Resin Type: |
|
Description: | Nylene 6250L is a low viscosity nylon 6/12 molding resin.  This material us used in applications requiring  good electrical insulation properties.  When molding, Nylene 6250L has high flow characteristics at minimum temperatures. |
Properties | ASTM/ISO Procedure | Unit | English | SI | |
---|---|---|---|---|---|
Physical | |||||
Relative Viscosity | ISO 307 Sulfuric Acid | n/a | 2.4 | ||
Mechanical | |||||
Elongation @ Break | D638 | % | 250 | ||
Tensile Strength @ Yield | D638 | psi (MPa) | 9427 | 65 | |
Physical | |||||
Density | ISO 1183 | lb/in³ (g/cm³) | 0.0376 | 1 | |
Thermal | |||||
Melt Point (DSC) | ASTM D3418 | °F (°C) | 423 | 217 | |
Mechanical | |||||
Flexural Modulus | D790 | psi (MPa) | 290000 | 2,000 |
Notes: | Testing conducted on dry-as-molded specimens at 73°F (22.8°C} |
Pressure | psi |
---|---|
Injection | 4 – 12,000 |
Hold | 3 – 9,000 |
Back | 0 – 50 |
Maximum Moisture: 0.2%
Mold Temperature:
150-250 °F, highly filled grades require >175 °F to obtain the best overall surface appearance
Residence Time:
Should not exceed 6 minutes, less with higher melt temps.
Shot Size:
Should be between 25-75% of barrel capacity.
Fill Rate:
Fast fill rates are suggested for best surface appearance.
Regrind Level:
Typically no more than 25% is recommended, with higher levels possible for unfilled grades depending on the end use requirements. Make certain regrind is properly dried to virgin moisture levels.
Drying Temp.
Nylene 6/12 – 150-180 °F for 2-4 hours
Fillers/Reinforcements:
Approvals & Recognition:
Automotive Colors:
Disclaimer
Nylene does not guarantee the accuracy of this information or the suitability of this product for any given application or usage situation. These values are based on test specimens and should not be used to establish specification limits or fabricate tooling.