TDS Ref ID: 1532
Date Updated May 27, 2024
Resin Type: |
|
Description: |
|
Properties | ASTM/ISO Procedure | Unit | English | SI | |
---|---|---|---|---|---|
Physical | |||||
Specific Gravity | D792 | n/a | 1.09 | 1.09 | |
Mechanical | |||||
Elongation | D638 | % | 250 | ||
Thermal | |||||
Melt Point | D3418 | °F (°C) | 426 | 219 | |
Mechanical | |||||
ARM Drop Impact, C.T., -30°C | ARM | ft-lb (N) | 90 | 400 | |
Tensile Strength | D638 | psi (MPa) | 7,600 | 52 | |
Flexural Modulus | D790 | psi (MPa) | 270,000 | 1,862 | |
ARM Drop Impact, C.T., -40°C | ARM | ft-lb (N) | 70 | 311 | |
Notched Izod @ -40°C | D256 | ft-lb/in (J/m) | 3.5 | 187 | |
Notched Izod, R.T. | D256 | ft-lb/in (J/m) | No Breaks | ||
ARM Drop Impact, R.T | ARM | ft-lb (N) | 150 | 667 |
Notes: | Testing conducted on dry-as-molded specimens at 73°F (22.8°C} |
Zone | °F (C°) |
---|---|
Feed | 420-445 (216-229) |
Transition | 435-465 (224-241) |
Metering | 445-475 (229-246) |
Die | 445-475 (229-246) |
Melt Temp. | 455-489 (235-254) |
Line Rate | pph-rpm |
---|---|
21/2" extruder | 1.5-1.9 |
31/2" extruder | 3.5-4.5 |
41/2" extruder | 6.5-7.5 |
Residence Time: Screw should not be left idle for more than 3-4 minutes with melt in the barrel. Excess residence will be visible as black carbon specs in the melt.
Regrind Level: Typically, up to 25% is recommended but higher levels are possible with little or no effect on flow and finish.
Drying Temperature: Although Nylene resins are packaged and delivered in a low moisture state, it is good material handling practice to use a hopper dryer to maintain dryness. Should pre-drying be necessary, use settings of 180 °F (82.2°C) air at dew point of -40 at a rate of 1 cu. ft. / hour per pound of resin and a residence time of 2-4 hours.
Cooling and Sizing: While both air and water can be used as the cooling medium, air is preferred. The use of air allows additional time for sizing and reduces residual stress. This aids in reducing warpage, especially in profiles with varying wall sections. If water is used, heat the first section to above 100 °F (38°C) to reduce quenching and residual stress.
Die Design: Draw down of 30% is typical for all dimensions except wall thickness.
Land length: should be around 10x wall thickness.
Fillers/Reinforcements:
Approvals & Recognition:
Automotive Colors:
Disclaimer
Nylene does not guarantee the accuracy of this information or the suitability of this product for any given application or usage situation. These values are based on test specimens and should not be used to establish specification limits or fabricate tooling.
Nylene USA | |
---|---|
Corporate HQ/Facility | |
Kentucky Facility |
Nylene Canada | |
---|---|
Ontario Facility | |
Canada Sales Office |
International | |
---|---|
South America | |
Europe/Middle East |