PA6/6 Injection Molding – Glass Reinforced >15%

Processing Considerations for PA6/6 Injection Molding – Glass Reinforced >15%

Recommended Processing Considerations: PA6/6 Injection Molding - Glass Reinforced >15%

Melt Temperature: Nylene PA6/6 melts at 490 °F (254°C), actual melt temperatures of 540-600 (282-316°C) are permissible, depending on residence time and shot size.

Mold Temperature: 120-200 °F (49-93°C), highly filled grades require 180-200 °F (82-93°C) to obtain the best overall surface appearance, higher temperatures will increase crystallinity.

Residence Time: should not exceed 6 minutes if possible, less with higher melt temperatures.

Shot Size: should be between 25-75% of barrel capacity.

Fill Rate: fast fill rates are suggested for best surface appearance.

Regrind Level: typically no more than 25% is recommended, with higher levels possible for unfilled grades depending on the end use requirements. Make certain regrind is properly dried to virgin moisture levels.

Drying Temperature: 150-180 °F (65-182°C) (for 2-4 hours, Nylene PA6/6 should be dried to less than 0.20% moisture for optimum performance. Drying longer than 4 hours or at higher temperatures may cause oxidation of the polymer or remove essential volatiles.

Products

ProductReinforcement/AdditivesFeaturesResin Type
Nylene 5120 HS
  • Glass Filled
  • Good chemical resistance
  • High heat resistance
  • Improved strength and stiffness
  • Nylon 6/6
Nylene 9110 G43
  • Glass Filled
  • High stiffness
  • High strength
  • Reduced moisture pick-up
  • Nylon 6/6
Nylene 4114-33 HS
  • Glass Filled
  • High stiffness
  • High toughness
  • Nylon 6/6
Nylene PA66G43LI BK
  • Glass Filled
  • Impact Modified
  • Excellent strength
  • Excellent surface appearance
  • High stiffness
  • Nylon 6/6
Nylene 5115 HS
  • Glass Filled
  • Heat Stabilizer
  • Good chemical resistance
  • High heat resistance
  • Improved strength and stiffness
  • Nylon 6/6
Nylene 5150
  • Glass Filled
  • High heat resistance
  • Very high strength and stiffness
  • Nylon 6/6
Nylene 6440 HS
  • Mineral Filled
  • Impact Modified
  • Excellent impact resistance
  • Nylon 6/6
Nylene 5140 HS
  • Glass Filled
  • Good chemical resistance
  • High heat resistance
  • High strength and stiffness
  • Nylon 6/6
Nylene 6140 HS
  • Mineral Filled
  • Heat Stabilizer
  • Heat resistance
  • High stiffness
  • Maximum stability
  • Nylon 6/6
Nylene 5145 HS
  • Glass Filled
  • Good chemical resistance
  • High heat resistance
  • Very high strength and stiffness
  • Nylon 6/6
Nylene 5143
  • Glass Filled
  • High stiffness
  • High tensile strength
  • Nylon 6/6
Nylene 5133 HSL
  • Glass Filled
  • Heat Stabilizer
  • Internally Lubricated
  • Chemical resistance
  • High heat
  • High stiffness
  • High tensile strength
  • Nylon 6/6
Nylene 5150 HS
  • Glass Filled
  • Heat Stabilizer
  • High tensile strength
  • Very high stiffness
  • Nylon 6/6
Nylene 5130 HS
  • Good chemical resistance
  • High heat resistance
  • High strength and stiffness
  • Nylon 6/6
Nylene 5135 HS
  • Glass Filled
  • Good chemical resistance
  • High heat resistance
  • High strength and stiffness
  • Nylon 6/6
Nylene 5133 HS
  • Glass Filled
  • Heat Stabilizer
  • Chemical resistance
  • High heat
  • High stiffness
  • High tensile strength
  • Nylon 6/6
Nylene 5133
  • Glass Filled
  • High stiffness
  • High strength
  • Nylon 6/6
Nylene 7215 HS BK
  • Glass Filled|Mineral Filled
  • Heat Stabilizer
  • Low warp
  • Nylon 6/6
Nylene 7215 HS
  • Glass Filled
  • Mineral Filled
  • Heat Stabilizer
  • Low warp
  • Nylon 6/6
Nylene 5125 HS
  • Glass Filled
  • Good chemical resistance
  • High heat resistance
  • Improved strength and stiffness
  • Nylon 6/6
1 / 212

Send Us A Message

United-states_flag_icon_round.svg Nylene USA
Corporate HQ/Facility
Kentucky Facility
canada-svgrepo-com.svg Nylene Canada
Ontario Facility
Canada Sales Office
International Flag Icon Round International
South America
China
Malaysia
Europe/Middle East
Skip to content